Igama lomkhiqizo | Isobornyl methacrylate |
Isibizo | 2-methyl-,1,7,7-trimethylbicyclo(2.2.1)hept-2-ylester,exo-2-propenoicaci; 2-methyl-,1,7,7-trimethylbicyclo[2.2.1]hept-2-ylester,exo-2-Propenoicacid; 2-propenoicacid,2-methyl-,1,7,7,-trimethylbicyclo[9.2.1]hept-2-ylester,exo-; I-Lsobornyl methacrylate IBOMA; 1,7,7-trimethylbicyclo[2.2.1]hept-2-yl 2-methylprop-2-enoate; (1R,2S,4S)-1,7,7-trimethylbicyclo[2.2.1]hept-2-yl 2-methylprop-2-enoate; (1R,2R,4S)-1,7,7-trimethylbicyclo[2.2.1]hept-2-yl 2-methylprop-2-enoate; IBOMA |
Ifomula yamangqamuzana | C14Hamashumi amabili nambiliO2 |
Isisindo samangqamuzana | 222.32 |
I-CAS NO. | 7534-94-3 |
Impahla |
Ukubukeka | Icacile futhi isobala | Okuqukethwe kwe-ester | >99% |
Umswakama | ≤0.1% | Ukuminyana | 0.985(g/cm3) |
I-Viscosity | 10-15(25℃)mPa·s | Iphoyinti le-Flash | 119℃ |
I-temperature ye-Glass Transitionmg/kg | 170 ℃ | Inkomba ye-refractive | 1.47 (25℃) |
|
Inkomba yekhwalithi | Ubumsulwa ≥99% Okuqukethwe komswakama≤0.1% |
Ukusetshenziswa |
1. Thermoplastic acrylic resin 2. I-powder enamathela inhlaka 3. Thermosetting acrylic resin 4. I-resin ye-acrylic enezingxenye ezimbili 5. Ingcina 6. Isilungisi sepulasitiki 7. I-fiber optical yepulasitiki
|
Ukupakisha | Izindlela ezimbili zokupakisha, isigubhu sepulasitiki esingu-25Kg kanye nesigubhu sensimbi esingu-200Kg sepulasitiki. |
Isitoreji kanye nezinto zokuhamba | I-IBOMA ayiyona eyamakhemikhali avuthayo, kodwa kufanele igcinwe endaweni yokugcina impahla enomoya omuhle, igweme ilanga eliqondile, nokuhlukaniswa nomthombo wokushisa ukuze kuvinjelwe ukuwohloka kwe-poly ephezulu. |
|