Ihe nkwekorita ọhụrụ na-emepe emepe dị ka HTPB, EHTPB, ATBN, HTBN, CTBN...
Anyị factory ọhụrụ mepụtara na bonding mmadụ, dị kaHTPB,EHTPB,ATBN,HTBN,CTBN, wdg...
MakaHTPB dị ka ezigbo diaphaneity, ala viscosity, ịka nká na-eguzogide, obere okpomọkụ arụmọrụ, Hydrolysis eguzogide, acid na alkali eguzogide, eyi iguzogide na magburu onwe eletriki mkpuchi Njirimara na nhazi arụmọrụ dị mma. Enwere ike iji HTPB mee ihe na nrapado, ihe mkpuchi, mkpuchi, ihe ndị na-emepụta ihe (HTPB+AP+Al), na ọtụtụ ụdị ojiji.
Klas dị iche iche dị ka ndị a:
Ihe | Ọkwa I | Ọkwa II | Ọkwa III | Ọkwa IV | Ọkwa V | ỌkwaVI |
Ọdịdị | Mmiri mmiri na-enweghị agba ma ọ bụ na-acha odo odo na-acha uhie uhie, enweghị adịghị ọcha a na-ahụ anya | |||||
Uru Hydroxyl (mmol/g) | 0.47-0.53 | 0.54-0.64 | 0.65-0.70 | 0.71-0.80 | 0.81-1.00 | 1.00-1.40 |
Viscosity (40 ℃ Pa.s) | 9.5 | 8.5 | 4.0 | 3.5 | 5.0 | 3.0 |
Peroxide mass ụmụ irighiri, %≤ | 0.04 | 0.04 | 0.05 | 0.05 | 0.10 | 0.10 |
Mmiri, wt%≤ | 0.05 | 0.05 | 0.05 | 0.05 | 0.10 | 0.10 |
Ọdịnaya na-agbanwe agbanwe,%≤ | 0.5 | 0.5 | 0.65 | 0.65 | 1.0 | 1.0 |
Ibu molekụla | 3800-4600 | 3300-4100 | 3000-3600 | 2700-3300 | 2300-3000 | 1200-1800 |
Mara: Anyị nwere ike ijikọụdị ọ bụla nke HTTPBdị ka ndị ahịa nkọwa ndị ọzọ arịrịọ. |
MakaEHTPB , EHTPB bụ HTPB molecular yinye nke na-ewebata epoxy iche iche, nke nwere uru dị ka mmanụ iguzogide, ịka nká, ezi nghọta, na ezi ala-okpomọkụ arụmọrụ. The hydroxyl dị iche iche na njedebe nke molekul yinye na hydroxyl dị iche iche na molekul yinye Otu epoxy otu reactive ìgwè nwere ike gwọọ dị iche iche isocyanates na epoxy curing agents Na-agwọ ọrịa polymer nwere ezigbo anụ ahụ na kemịkalụ Njirimara, magburu onwe adhesion ike. dị iche iche na-abụghị ọla ihe dị ka ọla na iko, ezi dielectric Njirimara, ala shrinkage ọnụego, na hardness High ogo, ike ka alkali na ọtụtụ mpịakọta, nwere ike budata mma n'ibu Njirimara, nrapado ike, na okpomọkụ iguzogide nke polyurethane ihe.
Enwere ike iji EHTPB mee ihe maka nrapado, ihe mkpuchi, mkpuchi, mgbaka epoxy resin, polyurethane elastomer, wdg.